Ferritic Stainless Steels
Contain 16-30% Cr - can be brittle at room temperature
Do not harden when welded
Suffer from excessive grain growth when heated to 950-1100oC
Preheat to 50-250oC
- reduces HAZ cooling rate
- maintains material above ductile/brittle transition temperature
- anneals residual stresses