Nature of Fatigue Cracks
Crack originates at stress concentrations
- Crack grows with each stress cycle until there is insufficient material left to support the load and fracture occurs
In welds there are always sufficient small defects to nucleate a fatigue crack in the first few cycles (i.e. no incubation period)