Porosity
Uniform porosity from exsolution of dissolved gases
Restart porosity - from unstable arc at weld start (incomplete protection, poor welding technique)
Surface porosity - from excessive contamination (grease, dampness, atmosphere) or sometimes high sulphur in consumables
Crater pipes - from shrinkage crater at end of weld run