Reheat Cracking
Chromium, molybdenum and vanadium containing steels most susceptible
Prevented by
- Heat treat with a low temperature soak followed by rapid heating to high temperature
- Grinding or peening weld toes after welding
- Use two-layer welding technique to refine the coarse grained HAZ structure
- Use non-susceptible weld metal