Thermal Hardening
Hard layer produced on plain carbon steels by rapid heating of the surface followed by water or oil quenching
- medium carbon content required (0.3-0.6%)
- Martensite formed on quenching
- Tempering (e.g.1h at 160oC) is necessary after quenching to reduce brittleness and relieve stresses