Induction Hardening Steels (cont.)
Volume changes occur in the hardened layers
- ~4% expansion from austenite to Martensite transformation on cooling
- depends on alloy content and bar diameter
Volume changes generate residual stresses and can lead to cracks
- tempering necessary without delay after hardening
- more carbon=more cracks