CVD Tool Substrates
Early coated cemented carbides were prone to catastrophic brittle failure at high feed rates in cutting
Increasing the cobalt content from 6% can improve this but tool tip blunting then occurs from reduced strength
In the late 1970s it was found that increasing the surface cobalt enriched zone to 10-30?m provided the necessary toughness without loss of strength